Tulsimer ?T-46 (陽)

Tulsimer ?A-33 (陰)

型式(Type)

強酸性陽離子交換樹脂 (Strong acid Cation exchange resin)

強堿性陰離子交換樹脂 (Strong base Anion exchange resin)

主體結(jié)構(gòu)(Matrix Structure)

苯乙烯(Cross linked polystyrene)

苯乙烯(Cross linked polystyrene)

功能基 (Functional Group)

硫酸基(Sulfonic acid)

4級胺(Quaternary ammonium Type I)

物理性貭(Physical Form)

球狀顆粒(Moist spherical beads)

球狀顆粒(Moist spherical beads)

離子型式(Ionic form supplied)

氫(Hydrogen)

氫氧(Hydroxide)

粒徑范圍(U.S.mesh in wet)

16 to 50

16 to 50

粒度范圍 (Particle Size)

0.3 to 1.2 mm

0.3 to 1.2 mm

微粒含量(Fines Content)

穿過US 50 Mesh小于0.5% (Less than

0.5% passing through 50 U.S.mesh)

穿過US 50 Mesh小于0.5% (Less than

0.5% passing through 50 U.S.mesh)

總交換容量

(Total Exch. Capacity)

1.8 meq/ml minimum of

99% in hydrogen form

1.0 meq/ml minimum of 90% in hydroxide

form and less than 1% in chloride form

拋光樹脂回收、拋光樹脂進(jìn)水要求：
拋光樹脂通常用于超純水樹脂中，產(chǎn)水質(zhì)量通常能夠達(dá)到18兆歐以上，為了產(chǎn)水質(zhì)量，通常對進(jìn)水要求也比一般的樹脂高一些。一般正常使用的情況下進(jìn)水中不能含有膠體、油脂、金屬離子、有機物等物質(zhì)，PH值不能超過14，進(jìn)水溫度不能超過樹脂的使用溫度，壓力不得超過0.5Mpa，懸浮物應(yīng)低于5mg/L。為了達(dá)到這些要求，通常會在拋光樹脂前面加入石英砂、活性炭、精密過濾器等過濾裝置，如果產(chǎn)水要求質(zhì)量非常高，則需要使用反滲透+EDI膜殼進(jìn)行處理。大致的工藝流程為原水→原水加壓泵→多介質(zhì)過濾器→活性炭過濾器→軟水器→精密過濾器→反滲透膜→EDI模塊→拋光混床樹脂→微孔過濾器→用水點。
拋光樹脂是由高度純化、轉(zhuǎn)型的H型陽樹脂和OH型陰樹脂混合而成,如果裝填和操作得當(dāng),在初的周期中即可制備出電阻率大于18.0MΩ·cm和TOC小于10ppb的超純水,無需化學(xué)再生。
樹脂開封后長時間暴露在空氣中會吸收二氧化碳,從而影響產(chǎn)品的性能及使用。因此一旦拆包需盡快使用。不使用部分須小心密封,存放于避光陰涼處,環(huán)境溫度以5-40℃為宜。
在運輸、儲存和裝填過程中,任何無機或有機物質(zhì)的接觸都會使樹脂受到污染,從而降低出水水質(zhì);影響運行工況。因此所有用于裝填、操作的設(shè)備和水不會污染樹脂。
向樹脂罐中加水使液位高度在200-300mm或僅沒過底部布水管,以防止裝填樹脂過程中底部排水裝置受到?jīng)_擊。但如果設(shè)備尺寸較小而擬采用樹脂以漿水混合的方式填裝也可不必事先加水。
(1)禁止用任何機械泵轉(zhuǎn)移樹脂,許多類型的泵都會對樹脂造成損害或帶來一些污染;

(2)樹脂裝填過程中,不要同時打開兩袋以上的樹脂。以大限度減少樹脂接觸空氣的時間,也使外來雜質(zhì)污染樹脂的可能性降到低;